Diaz Technologies supplies post-consumer and post-industrial recycled polypropylene grades, sourced and processed for injection molding and extrusion applications.
SKU 530035
Homopolymer Polypropylene
37 Melt Flow Rate | 0.90 Specific Gravity
SKU 530035 is a homopolymer polypropylene supplied in natural pellet form. This material offers a nominal melt flow rate of 37 g/10 min, a specific gravity of 0.90 and consistent physical properties suitable for injection molding applications.
Material Profile
- Polymer
- Homopolymer
- Recycled content category
- Mixed Rigids
- Primary application
- Injection Molding
- Appearance
- Transparent with Hue
- SKU
- 530035
Typical Test Results
| Property | Test Method | Unit | Typical Value |
|---|---|---|---|
| Melt Flow Rate (230°C / 2.16 kg) ASTM D1238 | ASTM D1238 | g/10 min | 37 |
| Specific Gravity ASTM D792 | ASTM D792 | g/cm³ | 0.90 |
| Tensile Strength ASTM D638 | ASTM D638 | psi | 4,200 |
| Flexural Modulus (Tangent Method) ASTM D790 | ASTM D790 | ksi | 160 |
| Notched Izod Impact ASTM D256 | ASTM D256 | ft-lb/in | 0.60 |
Key Features
- Transparent pellets with a hue
- Homopolymer Polypropylene
- 37 melt flow rate
- Suitable for injection molding applications
- Passed visual contamination inspection
Technical Note
The material is supplied in pellet form and has been evaluated for melt flow, density, mechanical properties, and visual quality to support processing consistency and performance.
SKU 230109
Recycled Homopolymer Polypropylene
Post-Industrial Recycled Material | Injection Molding
Recycled homopolymer polypropylene intended primarily for injection molding applications. The supplied source identifies the material as post-consumer recycled (PCR) with a mixed-color appearance.
Material Profile
- Polymer
- Homopolymer polypropylene
- Recycled content category
- PCR - Yes
- Primary application
- Injection molding
- Appearance
- Mixed-color pellets
- SKU
- 230109
Typical Test Results
| Property | Test Method | Unit | Typical Value |
|---|---|---|---|
| Melt Index (190°C / 2.16 kg) ASTM D1238 | ASTM D1238 | g/10 min | 9.0 |
| Density ASTM D792 | ASTM D792 | g/cm³ | 0.95 |
| Notched Izod Impact Strength ASTM D256 | ASTM D256 | ft-lb/in | 0.75 |
| Tensile Strength ASTM D638 | ASTM D638 | MPa | 26.0 |
| Tensile Strength ASTM D638 | ASTM D638 | psi | 4,000 |
| Elongation at Yield ASTM D638 | ASTM D638 | % | 15 |
| Flexural Modulus ASTM D790 | ASTM D790 | MPa | 1,300 |
| Flexural Modulus ASTM D790 | ASTM D790 | psi | 190,000 |
| Ash Content ASTM D5630 | ASTM D5630 | % | 2.0 |
| Color | – | – | Mixed |
Key Features
- Recycled homopolymer polypropylene
- Post-Consumer Recycled (PCR)
- Intended primarily for injection molding
- Mixed-Color Pellet Form
- Feedstock: FIBC
Technical Note
Values shown are typical laboratory results from the supplied source data and are not product specifications.
SKU 2301100
HPP Black High Flow
115 Melt Flow Rate | High Flow Homopolymer
HPP Black High Flow is a high flow homopolymer polypropylene supplied in black pellet form. This material offers a melt flow rate of 115 g/10 min and consistent physical properties suitable for injection molding applications.
Material Profile
- Polymer
- Homopolymer
- Recycled content category
- Carpet from Convention Shows
- Primary application
- Injection Molding
- Appearance
- Black Pellets
- SKU
- 2301100
Typical Test Results
| Property | Test Method | Unit | Typical Value |
|---|---|---|---|
| Melt Flow Rate (230°C / 2.16 kg) ASTM D1238 | ASTM D1238 | g/10 min | 115 |
| Specific Gravity ASTM D792 | ASTM D792 | g/cm³ | 0.90 |
| Tensile Strength ASTM D638 | ASTM D638 | psi | 3,300 |
| Tensile Elongation ASTM D638 | ASTM D638 | % | 2.8 |
| Flexural Strength ASTM D790 | ASTM D790 | psi | 3,800 |
| Flexural Modulus (Tangent Method) ASTM D790 | ASTM D790 | psi | 115,000 |
| Notched Izod Impact ASTM D256 | ASTM D256 | ft-lb/in | 0.92 |
| Ash Content ASTM D2584 | ASTM D2584 | % | 0.0 |
Key Features
- High Flow Homopolymer Polypropylene
- Excellent Mold Filling
- Designed for Injection Molding
- Consistent Processing Performance
- Black Pre-Colored Compound
- Passed visual contamination inspection
SKU 230103
Recycled Copolymer Polypropylene
Post-Industrial Recycled Material | Injection Molding and Extrusion
Recycled copolymer polypropylene is intended for injection molding and extrusion applications. The material is supplied as black/grey pellets and is identified as post-consumer recycled (PCR).
Material Profile
- Polymer
- Copolymer polypropylene
- Recycled content category
- PCR - Yes
- PP content
- 100%
- Appearance
- Black/Grey pellets
- SKU
- 230103
Typical Test Results
| Property | Test Method | Unit | Typical Value |
|---|---|---|---|
| Melt Index (190°C / 2.16 kg) ASTM D1238 | ASTM D1238 | g/10 min | 3 |
| Density ASTM D792 | ASTM D792 | g/cm³ | 0.95 |
| Notched Izod Impact Strength ASTM D256 | ASTM D256 | ft-lb/in | 3.0 |
| Tensile Strength ASTM D638 | ASTM D638 | psi | 3,200 |
| Elongation at Break ASTM D638 | ASTM D638 | % | 20 |
| Flexural Modulus ASTM D790 | ASTM D790 | psi | 150,000 |
| Flexural Strength ASTM D790 | ASTM D790 | psi | 2,800 |
| Ash Content ASTM D5630 | ASTM D5630 | % | 2.0 |
| Specific Gravity ASTM D792 | ASTM D792 | – | 0.95 |
| PP Content | – | % | 100 |
| Color | – | – | Black/Grey |
Key Features
- Recycled Copolymer polypropylene
- Post-Consumer Recycled (PCR)
- Suitable for injection molding and extrusion
- 100% polypropylene content
- Black/Grey pellet form
- Feedstock: FIBC
Technical Note
Values shown are typical laboratory results from the supplied source data and are not product specifications.
For availability, samples, pricing, or technical assistance, contact Susan Blackson, Director of Business Development, at ar.moxey@diaztech.net.
Disclaimer: The data presented herein represents test results obtained from laboratory evaluation and is believed to be accurate. Values should not be construed as product specifications or warranties of performance. Users are responsible for determining suitability for their specific applications, processing conditions, and regulatory requirements.